Vacuum Melt Alloy

Nickel Base Equiax
Nickel Base Equiax
C Cr Ni Co Mo W Nb / Cb Ta Ti Al B Zr Hf Fe Re Other Density gm/cm3 Density lb/in3 Approximate Melting
Range °F 
Approximate Melting Range °C 
B 1900 0.10 8 Bal 10 6 - - 4.25 1 6 0.015 0.07 -   - 8.22 0.297 2325-2375 1274-1302
B 1900 +HF 0.10 8 Bal 10 6 - - 4.25 1 6 0.015 0.1 1.1   - 8.25 0.298 -
B 1910 0.15 10 Bal 10 3 - - 7.25 1.25 6 0.015 0.1 -   - - 2400 1316
CM 681 LC® .1 5.5 Bal 9 - 8.5 - 6 .15 - - .01 1.5 5.75 3  - 8.91 0.322 - -
NI - X .10 21.75 Bal 1.5 9 0.6 - - - - - - - 18.5   1.0xMn
1.0xSi
8.21 0.296 2300-2470 1260-1354
IN 100 0.16 10 Bal 15 3 - - - 4.75 5.5 0.015 0.04 -   .8V 7.75 0.280 2350-2435 1288-1335
IN 625 0.20 21.6 BAl - 8.7 - 3.9 - 0.2 0.2 - - -   - 8.44 0.305 2350-2460 1288-1349
IN 713 C 0.10 13.5 BAl - 4.5 - 2 - 0.8 6 0.010 0.06 -   - 7.91 0.286 2300-2350 1260-1288
IN 713 LC 0.06 12 Bal - 4.3 - 2 - 0.7 5.8 0.007 0.06 -   - 8.00 0.289 2350-2410 1288-1321
IN 718 0.05 19 52.5 - 3 - 5 - 0.9 0.55 0.005 - - Bal   8.22 0.297 2300-2450 1260-1343
IN 738 LC 0.09 16 Bal 8.5 1.7 2.5 0.8 1.7 3.5 3.5 0.010 0.05 -   - 8.11 0.293 2250-2400 1231-1316
IN 738 C 0.17 16 Bal 8.5 1.7 2.5 0.8 1.7 3.5 3.5 0.010 0.1 -   - 8.11 0.293 -
IN 792 0.12 12.4 Bal 9 1.9 3.8 - 3.9 4.5 3.1 0.020 0.1 -   - 8.25 0.298 -
IN 792+Hf 0.11 12.2 Bal 9 2 3.8 - 4 4 3.5 0.015 0.1 .50 - .85     - -   2270-2400 1240-1315
IN 939 0.15 22.4 BAl 19 - 1.6 1 1.4 3.7 1.9 0.010 0.1 -   - 8.17 0.295 2255-2440 1235-1338
Mar M 002* 0.15 9 Bal 10 - 10 - 2.5 1.5 5.5 0.015 0.05 1.5   - 8.53 0.308 -
Mar M 004 0.05 12 Bal - 4.5 - 2 - 0.6 5.9 0.015 0.05 1.3   - 8.02 0.290 2425 1329
Mar M 200 0.15 9 Bal 10 - 12.5 1.8 - 2 5 0.015 0.05 - - - - 8.53 0.308 2400-2500 1315-1370
Mar M 246 0.15 9 Bal 10 2.5 10 - 1.5 1.5 5.5 0.015 0.05 -   - 8.44 0.305 2400-2450 1315-1343
Mar M 247* 0.16 8.2 Bal 10 0.6 10 - 3 1 5.5 0.015 0.05 1.5   - 8.54 0.308 2380-2490 1305-1365
Mar M 421 0.15 15.5 Bal 9.5 2 3.8 2 - 1.8 4.3 0.015 0.05 -   - 8.08 0.292 2350-2450 1288-1343
CM 247 LC* 0.07 8 Bal 9 0.5 10 - 3.2 0.7 5.6 0.015 0.01 1.4   - 8.54 0.308 -
CM 681 LC                 8.91 0.322  
Rene' 41 0.09 19 Bal 11 9.75 - - - 3.15 1.65 0.005 - -   - 8.25 0.298 2400-2500 1315-1371
Rene' 77 0.07 14.6 Bal 15 4.2 - - - 3.3 4.3 0.015 0.04 -   - 7.91 0.286 2200-2550 1204-1400
Rene' 80 0.16 14 Bal 9.5 4 4 - - 5 3 0.015 0.03 -   - 8.16 0.295 -
Rene' 95 0.15 14 Bal 8 3.5 3.5 3.5 - 2.5 3.5 0.010 0.05 -   - 8.19 0.296 -
Rene' 125 0.11 9 Bal 10 2 7 - 3.8 2.5 1.4 0.017 0.05 -   - 8.53 0.308 -
Rene' 220 0.02 18 Bal 12 3 - 5 3 1 0.5 0.010 - -   - - 2280-2455 1250-1350
U 500 0.07 19 Bal 18 4 - - - 3 3 0.007 - -   - 8.02 0.290 -
U 700 0.07 15 Bal 18.5 5 - - - 3.5 4.4 0.025 - -   - 7.91 0.286 2200-2550 1204-1400
Waspaloy 0.07 19.5 Bal 13.5 4.25 - - - 3 1.35 0.005 - -   - 8.19 0.296 2425-2475 1329-1357
C263 0.06 20 Bal 20 5.9 - - - 2.15 0.45 0.001 - -   - 8.36 0.302 -
C 1023 0.16 15.5 Bal 10 8.5 - - - 3.6 4.2 0.006 - -   - - -
GMR 235 0.15 15.5 Bal - 5.3 - - - 2 3 0.060 - - 10    .3 Mn, .6 Si 8.00 0.289 -  
GTD 111 0.10 14 Bal 9.5 1.6 3.8 - 2.8 4.9 3 0.012 0.02 -   - 8.17 0.295 -
GTD 222 0.10 22.5 Bal 19 - 2 0.8 1 2.3 1.2 0.005 0.012 -   - - 2355-2500 1290-1370
* Also used as DS                    


Nickel Base Directionally Solidified

Nickel Base DS C Cr Ni Co Mo W Nb/Cb Ta Ti Al B Zr Hf Fe Re Other Density gm/cm3 Density lb/in3 Approximate Melting
Range °F 
Approximate Melting
Range °C
Mar M 200+Hf  0.14 9 Bal 10 - 12 1 - 2 5 0.015 - 0.8-1.9   - 8.61 0.311 -
Mar M 002 0.15 9 Bal 10 - 10 - 2.5 1.5 5.5 0.015 0.05 1.5   - 8.53 0.308 -
Mar M 247 0.16 8.2 Bal 10 0.6 10 - 3 1 5.5 0.015 0.05 1.5   - 8.54 0.308 -
PWA 1426 0.10 6.5 Bal 12 2 6 - 4 - 6 0.015 0.03 1.5 3 8.60 0.310 -
Rene' 142 0.12 6.8 Bal 12 2 5 - 6 - 6.2 0.015 0.02 1.5 3 8.60 0.310 -
CM 186 LC* 0.07 6 Bal 9 0.5 8 - 3 0.7 5.7 0.015 0.005 1.4 3 8.70 0.314 2400-2520 1315-1380
CM 247 LC 0.07 8 Bal 9 0.5 10 - 3.2 0.7 5.6 0.015 0.01 1.4   - 8.54 0.308 2385-2510 1310-1375
Rene' 80 H 0.16 14 Bal 9 4 4 - - 4.7 3 0.015 0.01 0.8      
GTD 111 M 0.10 14 Bal 9.5 1.6 3.8 - 2.8 4.9 3 0.012 - -      
*Also used as single crystal      


Nickel Base Single Crystal

Nickel Base Single Crystal C Cr Ni Co Mo W Nb/Cb Ta Ti Al B Zr Hf Fe Re Other Density gm/cm3 Density lb/in3 Approximate Melting
Range °F
Approximate
Melting
Range °C
PWA 1480 - 10 Bal 5 - 4 - 12 1.5 5 0.003 - - - 8.70 0.314 2350-2450 1290-1340
PWA 1484 - 5 Bal 10 1.9 5.9 - 8.7 - 5.65 - - 0.1 3   8.95 0.323 -  
PWA 1487 - 5 Bal 10 1.9 5.9   8.4   5.65   0.25 3 Y 0.013 8.95 0.323  
Rene' N4 - 10 Bal 8 2 6 0.5 5 3.5 4.2 - - 0.2   8.56 0.309 -  
Rene' N5 - 7 Bal 8 2 5 - 6 - 6.2 - - 0.2 3   8.63 0.312 -  
Rene' N6 - 4 Bal 12 1 6 - 7 - 5.8 - - 0.2 5   8.97 0.324 -  
CMSX-2 - 8 Bal 5 0.6 8 - 6 1 5.6 - - -   8.56 0.309 2415-2500 1320-1370
CMSX-3 - 8 Bal 5 0.6 8 - 6 1 5.6 - - 0.1   8.56 0.309 2420-2510 1325-1375
CMSX-4 - 6.5 Bal 9 0.6 6 - 6.5 1 5.6 - - 0.1 3   8.70 0.314 2415-2515 1320-1380
CMSX-4 [ULS][La+Y] - 6.5 Bal 9 0.6 6 - 6.5 1 5.6 - - 0.1 3 La+Y 0.002 8.70 0.314  
CMSX-4 (B/C)[MK4] 0.04 6.5 Bal 9 0.6 6 - 6.5 1 5.6 0.006 - 0.2 3   8.70 0.314  
CMSX-6 - 10 Bal 5 3 - - 2 4.7 4.8 - - 0.1   7.98 0.288 -  
CMSX-10K - 2 Bal 3 0.4 5 0.1 8 0.2 5.7 - - 0.03 6   9.05 0.327 2480-2575 1360-1410
CMSX-10N - 1.5 Bal 3 0.4 5 0.05 8 0.1 5.8 - - 0.03 7     2480-2575 1360-1410
CMSX 486 0.07 5 Bal 9 0.7 9 - 4.5 0.7 5.7 0.015 0.005 1 3   8.85 0.319 -  
SRR 99 - 8 Bal 5 - 10 - 3 2.2 5.5 - - - - 8.56 0.309 -  
RR 2000 - 10 Bal 15 3 - - - 4 5.5 - - - 1 V 7.87 0.284 -  
AM 1 - 8 Bal 6 2 6 - 9 1.2 5.2 - - - - 8.59 0.310 -  
AM 3 - 8 Bal 6 2 5 - 4 2 6 - - - - 8.25 0.298 -  
SC 180 - 5 Bal 10 2 5 - 8.5 1 5.2 - - 0.1 3   8.84 0.319 -  


Cobalt Base
Cobalt Base C Cr Ni Co Mo W Nb/Cb Ta Ti Al B Zr Hf Fe Re Other Density gm/cm3 Density lb/in3 Approximate Melting
Range °F 
Approximate
 Melting Range °C 
FSX-414 0.25 29 10 Bal - 7.5 - - - - 0.010 - -     - 8.30 0.300 - -
Mar-M-302 0.85 21.5 - Bal - 10 - 9 - - 0.005 0.2 -     - 9.21 0.332 - -
Mar-M-509 0.60 23 10 Bal - 7 - 3.5 0.2 - - 0.5 -     - 8.85 0.319 2415-2525 1320-1385
Mar-M-918 0.05 20 20 Bal - - - 7.5 - - - 0.1 -     - -   -  
HS 21 0.25 27 3 Bal 5 - - - - - - - - 1    0.6 Mn, 0.6 Si -   -  
HS 31 (X-40) 0.50 25 10 Bal - 7.5 - - - - - - - 1.5   0.5 Mn, 0.5 Si 8.60 0.310 -  
X-45 0.25 25.5 10.5 Bal - 7 - - - - 0.010 - -     - 8.60 0.310 -  
HS 25 (L-605) 0.10 20 10 Bal - 15 - - - - - - -     - 9.13 0.330 -  
Haynes 188 0.10 22 22 Bal - 14 - - - - - - -     0.04 La 9.13 0.330 -  
AiResist 13 0.45 21 - Bal - 11 2 - - 3.5 - - -     0.1 Y -   -  
AiResist 213 0.18 19 - Bal - 4.7 - 6.5 - 3.5 - 0.15 -     0.1 Y -   -  
AiResist 215 0.35 19 - Bal - 4.5 - 7.5 - 4.3 - 0.13 -     0.17 Y -   -  
F-75 0.25 28 - Bal 5.5 - - - - - - - -     - 8.29 0.299 -  
WI-52 0.45 21 - Bal - 11 2 - - - - - - 2     8.88 0.321 -  
ECY 768 0.60 23 10 Bal - 7 - 3.5 0.2 - - - -     - -   -